Phase composition and electrical characteristics of nickel silicide Schottky contacts formed on 4H-SiC

Lookup NU author(s): Irina Nikitina, Dr Konstantin VasilevskiyORCiD, Dr Alton Horsfall, Professor Nick Wright, Professor Anthony O'Neill, Dr Christopher Johnson

Downloads

Full text for this publication is not currently held within this repository. Alternative links are provided below where available.


Abstract

4H-SiC Schottky diodes with nickel silicide contacts were formed by consecutive deposition of a titanium adhesion layer, 4 nm thick, and nickel, 100 nm thick, followed by annealing at temperatures between 600 and 750 degrees C. It was found that contacts with barrier heights of 1.45 eV which consist mainly of single nickel monosilicide (NiSi) phase were formed in the 600-660 degrees C temperature range, while annealing at around 750 degrees C led to the formation of Ni2Si Schottky contacts with barrier heights of 1.1 eV. Annealing at intermediate temperatures resulted in the nucleation of Ni2Si grains embedded in the NiSi film which were directly observed by micro-Raman mapping. It was shown that the thermodynamically unfavourable NiSi phase appeared in the 600-660 degrees C temperature range due to control of the Ni-SiC solid-state chemical reaction by nickel diffusion through the titanium diffusion barrier.


Publication metadata

Author(s): Nikitina I, Vassilevski K, Horsfall A, Wright N, O'Neill AG, Ray SK, Zekentes K, Johnson CM

Publication type: Article

Publication status: Published

Journal: Semiconductor Science and Technology

Year: 2009

Volume: 24

Issue: 5

ISSN (print): 0268-1242

ISSN (electronic): 1361-6641

Publisher: Institute of Physics Publishing Ltd.

URL: http://dx.doi.org/10.1088/0268-1242/24/5/055006

DOI: 10.1088/0268-1242/24/5/055006

Notes: Article no. 055006


Altmetrics

Altmetrics provided by Altmetric


Funding

Funder referenceFunder name
EP/D068827/1UK Engineering and Physical Sciences Research Council
TP/5/POW/6/I/H0486DTechnology Strategy Board

Share