Curing characteristics and internal stresses in epoxy coatings: Effect of crosslinking agent

Lookup NU author(s): Ahmed Abdelkader, Emeritus Professor Jim White

Downloads

Full text for this publication is not currently held within this repository. Alternative links are provided below where available.

Abstract

The development of internal stresses in a series of epoxy coatings prepared using five different crosslinking agents have been studied. The crosslinking agents were: H1, 4,4′ methylenedianiline (DDM); H2, diethylentriamine (DETA); H3, cycloaliphatic polyamine; H4, polyaminoimidazoline; and H5, polyamidoamine adduct. Four different post-cure treatments were applied and the dependence of internal stress on crosslinking agent and post-cure treatment was determined. Curing was followed by monitoring the FTIR epoxy band at 916 cm - 1 and the glass transition temperature was determined using DSC to assist interpretation of the measured values of internal stress. The internal stress was tensile in all of the materials at the end of each post-cure treatment. The stress magnitudes increased monotonically with post-cure temperature. The largest stresses were recorded with H1, H2 and H3 whereas the lowest stresses were recorded with H4 and H5, which both included a flexible aliphatic chain. The effects of ageing for extended periods in dry air and in humid air (52%RH and 97%RH) were also examined. Exposure to humid air almost always caused a reduction in the tensile stress and often produced compressive stresses, attributed to swelling due to water absorption. A comparison was made of the stresses formed in coatings applied to a thin substrate that was (i) free to bend during curing, post-curing and ageing, and (ii) prevented from bending ("restrained substrate"). The general trends in behaviour were in agreement but no simple relationship could be found between the stress magnitudes obtained by the two different test configurations. © 2005 Springer Science + Business Media, Inc.

Publication metadata

Author(s): Abdelkader AF, White JR

Publication type: Article

Publication status: Published

Journal: Journal of Materials Science

Year: 2005

Volume: 40

Issue: 8

Pages: 1843-1854

Print publication date: 01/04/2005

ISSN (print): 0022-2461

ISSN (electronic): 1573-4803

Publisher: Springer

URL: http://dx.doi.org/10.1007/s10853-005-1203-9

DOI: 10.1007/s10853-005-1203-9

Altmetrics

Share